    PRODUCT DATA SHEET

    Hi-Build Aluminum Coating L-2156

     

     

    Description

    Middle East Hi-build Aluminum Coating L-2156, a solvent base, high luster paint with leafing aluminum flakes and especial synthetic resin binder.

     

     

    Properties & Uses

    It is a high luster for steel substrates with good heat resisting properties. It may be used on wooden surfaces as well if desired.

     

     

    Particulars

    Colour

    Metallic Aluminum

    Solid Content

    28 ± 2% by volume

    Recommended Film Thickness

    Dry – 25  microns  / Wet 80 microns

    Theoretical Coverage

    Approximate 9 – 10 m2 / liter @ 25 microns DFT on smooth non absorbent surface

    Practical Coverage

    Reduce up by 20%

    Finish

    Gloss

     

     

    Application Details

    Tools / Method

    By brush, roller and conventional spray

    Thinner / Cleaner

    Middle East Thinner # 8005

    Drying Time

    Touch dry 4  hours / Through dry 8 hours

    Recoating Time

    After minimum 18 to 24 hours

     

    Surface Preparation

    Surface should be clean, dry and free from loose grits oil, grease, dust, etc. Apply to suitable primed and undercoated surfaces.

     

     

    Storage & Handling

    Storage

    Store in safe place, keep out of reach of children.

    Safety

    Flammable – Flash point above 40 ºC

    Shelf -life

    12 months in unopened container

     

     

     

    Disclaimer

    The information stated herein is to the best of our knowledge true, accurate and is given in good faith but without warranty. The user will be deemed to have satisfied himself independently as to the suitability of our products for his own particular purpose. The document will be updated at least two years. It is the user’s responsibility to ensure they have the current copy.

     

                                                                                         Issued Date : January 2010